The 2A14 aluminum round bar is a high-strength hard aluminum, It is an optimal material for high-strength structural components. After heat treatment (quenching and aging), it achieves strength close to that of hard aluminum while maintaining good machinability.
The 2A14 aluminum round bar is a high-strength hard aluminum, It is an optimal material for high-strength structural components. After heat treatment (quenching and aging), it achieves strength close to that of hard aluminum while maintaining good machinability. It is widely used in aerospace and various high-strength structures, making it a reliable choice for demanding applications requiring superior strength and durability.
|
Alloy |
2A14 Aluminum Round Bar |
|
Temper |
T4, T6, etc. |
|
Diameter Range (mm) |
30 mm - 200 mm |
|
Standard Length (mm) |
Custom, up to 6 meters
|
|
MOQ |
5 tons |
|
Tensile Strength |
≥ 430 MPa |
|
Yield Strength |
≥ 275 MPa |
|
Elongation |
≥ 10 % |
|
Hardness |
≥ 110 HB |
|
Key Features |
High Strength, Good Machinability, Excellent Wear Resistance |
For precision components, material consistency is critical. Our 2A14 aluminum round bars undergo strict ultrasonic testing to ensure they are free from internal cracks and impurities, with a uniform and dense structure. We provide complete Mill Test Certificates (MTCs), giving you full traceability of the chemical composition and mechanical properties for each batch, guaranteeing the safety and reliability of your products from the source.
Thanks to its excellent machinability, the 2A14 aluminum round bar performs exceptionally well in CNC machining. It allows for easy chip breaking and reduces tool wear, which effectively increases processing efficiency and lowers overall costs. This material is commonly specified for manufacturing critical high-strength parts such as aircraft structural rivets, engine impeller disks, and high-load shaft components. It serves as a reliable and durable core material for your most demanding applications.